Thanks guys. Because of my construction and method of built I will have to use the router this time
.
BWD do you use ABS or epoxy poured rail on your boards?

Hi Everybody,
What kind of bit do you recommend for routing edges? My project board is 11 oz. CF lay up with epoxy poured edge. I just want to avoid sanding as much as possible. Thanks for any suggestions.

Thanks for all the info.
I read somewere that Corecell T foam is better than A foam in less "dynamic stress" areas. Isn't kiteboard punished with constant dynamic stress on the water ?
kris

Nonce thanks for the links Ken does wind suck in Miami this summer as bad as it does in Melbourne? Thats probably why you have time to spend on this forum :) Thanks for the article. Board looks really good. So wat lay up did you use and what was the weight of carbon cloth that you used? thanks, Kris

Hi Kakanala
I am sorry to hear that. Thousands of people shape surfboards and work with fiberglass on a daily basis. I just want to give it a try and hopefully I will not get allergic to this stuff. I can afford buying a decent board or two but I just like the idea of building your own stuff.
cheers

I found that link very helpfull
http://freespace.virgin.net/cav.labs/

Hi everybody
I understand that carbon and fiberglass have different properties but theoretically what carbon cloth would be equal in strength of 21 oz. fiberglass layer on a kiteboard?
Thanks

Thanks for the info

Thanks Zfennel for the link,
Correct me if i am wrong, corecell is slightly better as far as compression. Does H80 have any advantages over Corecell?

Hi everybody,
any oppinions on which is better and why?