the rear stab profile needs to be flipped to work better. right now the way they are shown you have a lift lift set up. people have tried and they work but work better with lift and push set up And from what I have see and done. if you are building your first set of wings flat bottom front flat top ...

mine mast is 120mmx10.8mm out of mould finished 11.1 with clearcoat on it. square TE ( was sharp enough to cut) toned it down. My r&D rider didn't feel that much change. on thing you could do on your next mast rake the fuse ahead 1-2 degrees will help any bubbles to go up and not down if the AOA is ...

another one off to a new home
carbon with carbon foot hooks. ( they are just sitting on the board)

insider trading the fuse is 27" long and alum too

CGL that is what I thought too... I can see SS stepping on LP toes after them making a good foil for them already which is in the same town as head office.

good for moses to pick up a big contract like that congrats to the boys.
It does look really good too up close in some of those pics.

terrie

billie PM sent brother

it looks a lot like a guy out of cali foils. And for moses and sling shot... I think LP would be pissed if they did that. I think it is more likely a prototype that they are working on for SS

or you can get a set of carbon foot hooks.

Terrie
www.jellyfishboards.com

plum you are right in one manner about heat cured and reg resin.. One of the big difference is if you put a hand lay up mast in the sun on the beach it will get soft way before the heat cured one. This is were the heat cured ( pregreg or heat cure resin ) will over ride the hand layup... Will the ha...